Product information
Very Low Rotation.
Superior bending fatigue life when compared with conventional low rotation ropes.
Excellent resistance to crushing and abrasion particuarly on multi layer drums resulting from the compacted strands.
Reduced elongation results from increased steel content and the Dyform process.
ISO 4309 Rope Category No: 10-40mm RCN.23-2, 42-76mm RCN.31
- Features: Extremely strong low rotation Crane Hoist Rope.
- Material: High Carbon Steel
- Marking: According to standard, CE-marked, On Termination ID
- Finish: Galvanised or Ungalvanised
- Standard: EN 12385-4
- Fill factor: 0.76
- RCN: 23-2
Product FAQ
What surface finish and tensile strength does this steel wire rope have?
This steel wire rope has a Bright, Galvanized and is manufactured with a tensile strength of 1960, 1960, 2160, 2160 N/mm².A bright (uncoated) finish has no corrosion protection and is therefore primarily used in dry, indoor, or controlled environments. Bright wire ropes are generally selected for cost reasons. The galvanized coating provides corrosion protection through a zinc layer, making the rope suitable for outdoor use and humid operating conditions.
Does this steel wire rope have any special design or performance features?
This steel wire rope is compacted, resulting in a smoother surface, higher breaking load, and improved wear resistance compared to standard wire rope constructions. This steel wire rope is designed to be rotation resistant, minimizing torque and rotation under load. It is particularly suitable for lifting applications involving single-line operation or long lifting heights.
What is the construction, core type, and lay of this steel wire rope?
This steel wire rope is constructed with Multistrand strands.
It is manufactured with a steel core, offering higher structural stability, improved resistance to crushing, and reliable performance under heavy loads and multi-layer winding conditions.
It is manufactured with a right-hand lang lay (zZ), offering increased abrasion resistance and extended service life in applications where surface wear is a critical factor. It is manufactured with a left-hand lang lay (sS), providing enhanced wear resistance and longer service life where high surface durability is required.