Ropetex PERFORM 8CP
Product information
Ropetex PERFORM 8CP is a high-quality steel wire rope consisting of eight strands. The outer strands are compacted, and the core is separated from the outer strands by a plastic layer, reducing internal stress and giving it an excellent service life. Ropetex PERFORM 8CP is not rotation resistant.
Key product benefits
- Excellent lifetime
- Suitable for multi-layer drum spooling
- Very resistant against crushing
- Very abrasion resistant
- High breaking load (MBL)
- Plastic layer to reduce internal friction and stress while protecting the core
Main applications
- Hoist rope
- Auxiliary hoist rope
- Boom Hoist rope
- Luffing rope
- Trolley rope
- Pendant rope
- Grab rope
Standard: EN12385
Rope Category Numbers acc. to ISO4309:2017
- Ø 8 mm to 14 mm: RCN 04
- Ø 15 mm to 39 mm: RCN 09
- Ø 40 mm to 48 mm: RCN 11
- Temperature range: -40°C up to +60°C with standard lubricant
- Fill factor: 0,664
- Tolerance Ø: +2% to +4%
-
Container crane
-
Overhead cranes
-
Truck crane
-
Offshore crane
-
Deck crane
-
Harbour mobile crane
-
Ladle crane
-
STS crane
-
Straddle carrier
-
RTG
Product FAQ
What surface finish and tensile strength does this steel wire rope have?
This steel wire rope has a Galvanized and is manufactured with a tensile strength of 1960 N/mm².The galvanized coating provides corrosion protection through a zinc layer, making the rope suitable for outdoor use and humid operating conditions.
Does this steel wire rope have any special design or performance features?
This steel wire rope is compacted, resulting in a smoother surface, higher breaking load, and improved wear resistance compared to standard wire rope constructions. This steel wire rope features internal plastic filling, which improves lubrication retention, reduces internal wire friction, and enhances service life under dynamic loading conditions.
What is the construction, core type, and lay of this steel wire rope?
This steel wire rope is constructed with 8 strands.
It is manufactured with a steel core, offering higher structural stability, improved resistance to crushing, and reliable performance under heavy loads and multi-layer winding conditions.
It is manufactured with an ordinary right-hand lay (sZ), providing a balanced combination of flexibility, wear resistance, and stable handling. This is the most commonly used lay for general It is manufactured with an ordinary left-hand lay (zS), offering similar performance characteristics to right-hand ordinary lay but designed for specific directional or equipment requirement